SAE AMS5920
$78.00
$35.10
Save 55%
SAE AMS5920 Revision A, February 1, 2013
Cobalt-Nickel Alloy, Corrosion and Heat-Resistant, Round Bars 19Cr - 36Co -
25Ni - 7.0Mo - 0.50Cb (Nb) - 2.9Ti - 0.20Al - 9.0Fe Vacuum Induction Plus
Vacuum Consumable Electrode Melted Solution Heat Treated, Work Strengthened
and Aged, Modified Strength
Description / Abstract:
Form
This specification covers a corrosion and heat-resistant, work strengthened and aged cobalt-nickel-chromium alloy in the form of bars 2 inches (50.8 mm) and under in nominal diameter
Application
These bars have been used typically for parts, such as fasteners, requiring a room temperature minimum tensile strength of 170 ksi (1172 MPa) for use up to 850 °F (454 °C) in applications requiring high ductility to promote toughness and resistance to cracking under shock loading conditions, but usage is not limited to such applications. This alloy exhibits exceptionally good resistance to corrosion, crevice corrosion, and stress-corrosion cracking.
This specification covers a corrosion and heat-resistant, work strengthened and aged cobalt-nickel-chromium alloy in the form of bars 2 inches (50.8 mm) and under in nominal diameter
Application
These bars have been used typically for parts, such as fasteners, requiring a room temperature minimum tensile strength of 170 ksi (1172 MPa) for use up to 850 °F (454 °C) in applications requiring high ductility to promote toughness and resistance to cracking under shock loading conditions, but usage is not limited to such applications. This alloy exhibits exceptionally good resistance to corrosion, crevice corrosion, and stress-corrosion cracking.
SAE AMS5920 Revision A, February 1, 2013
Cobalt-Nickel Alloy, Corrosion and Heat-Resistant, Round Bars 19Cr - 36Co -
25Ni - 7.0Mo - 0.50Cb (Nb) - 2.9Ti - 0.20Al - 9.0Fe Vacuum Induction Plus
Vacuum Consumable Electrode Melted Solution Heat Treated, Work Strengthened
and Aged, Modified Strength