SAE AMS4310 Revision E, July 1, 2008
Aluminum Alloy, Rolled or Forged Rings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr
(7075-T651, 7075-T652) Solution Heat Treated, Mechanically Stress Relieved,
and Precipitation Heat Treated
Description / Abstract:
Form
This specification covers an aluminum alloy in the form of rolled or forged rings.
Application
These rings have been used typically for high strength machined parts where good stability is required during machining, but usage is not limited to such applications. These rings are not recommended for fusion welding.
Certain design and fabricating procedures may cause these rings to become susceptible to stress-corrosion cracking; ARP823 recommends practices to minimize such conditions.
Classification
Rings are classified by type of mechanical stress relief as follows:
7075-T651 Stress relieved by tension
7075-T652 Stress relieved by compression
Either type may be supplied, unless a specific type is ordered.
This specification covers an aluminum alloy in the form of rolled or forged rings.
Application
These rings have been used typically for high strength machined parts where good stability is required during machining, but usage is not limited to such applications. These rings are not recommended for fusion welding.
Certain design and fabricating procedures may cause these rings to become susceptible to stress-corrosion cracking; ARP823 recommends practices to minimize such conditions.
Classification
Rings are classified by type of mechanical stress relief as follows:
7075-T651 Stress relieved by tension
7075-T652 Stress relieved by compression
Either type may be supplied, unless a specific type is ordered.
SAE AMS4310 Revision E, July 1, 2008
Aluminum Alloy, Rolled or Forged Rings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr
(7075-T651, 7075-T652) Solution Heat Treated, Mechanically Stress Relieved,
and Precipitation Heat Treated