Inspection, Ultrasonic, Wrought Metals, Process for
Description / Abstract:
Purpose
The purpose of this standard is to provide uniform methods for the ultrasonic inspection of wrought metals and wrought metal products.
Application
The methods for ultrasonic inspection in this standard are applicable in the detection of flaws in wrought metals and wrought metal products having a cross section thickness equal to 0.250 inch or greater. Round bar and billet may use AMS2628 techniques and equipment for billet over 4.5 inches using the acceptance criteria of Table 6 of AMS-STD-2154. Wrought metals include forging stock, forgings, rolled billet or plate, extruded or rolled bars, extruded or rolled shapes, and parts made from them. Application of the methods in this standard is not intended for non-metals, welds, castings, or sandwich structures.
Wrought Aluminum Alloy Products
Requirements for ultrasonic inspection of aluminum alloy wrought products, except as noted below, shall be in accordance with ASTM B594:
Ultrasonic inspection of machined aluminum alloy parts shall be in accordance with this standard.
Classification
The ultrasonic inspection methods in this standard shall be classified as follows:
Type
I - Immersion method
II - Contact method
Class Five ultrasonic acceptance classes shall be as defined in Table 6.
The purpose of this standard is to provide uniform methods for the ultrasonic inspection of wrought metals and wrought metal products.
Application
The methods for ultrasonic inspection in this standard are applicable in the detection of flaws in wrought metals and wrought metal products having a cross section thickness equal to 0.250 inch or greater. Round bar and billet may use AMS2628 techniques and equipment for billet over 4.5 inches using the acceptance criteria of Table 6 of AMS-STD-2154. Wrought metals include forging stock, forgings, rolled billet or plate, extruded or rolled bars, extruded or rolled shapes, and parts made from them. Application of the methods in this standard is not intended for non-metals, welds, castings, or sandwich structures.
Wrought Aluminum Alloy Products
Requirements for ultrasonic inspection of aluminum alloy wrought products, except as noted below, shall be in accordance with ASTM B594:
Ultrasonic inspection of machined aluminum alloy parts shall be in accordance with this standard.
Classification
The ultrasonic inspection methods in this standard shall be classified as follows:
Type
I - Immersion method
II - Contact method
Class Five ultrasonic acceptance classes shall be as defined in Table 6.