SAE AMS5357 Revision D, June 1, 2017
Steel, Corrosion-Resistant, Investment Castings 15Cr - 4.6Ni - 0.22Cb -
2.8Cu Solution Heat Treated, Precipitation Hardenable
Description / Abstract:
Form
This specification covers a corrosion-resistant steel in the form of investment castings.
Application
These castings have been used typically for parts which will be machined in the solution heat treated condition and, after precipitation heat treatment, will require good corrosion resistance and strength up to 600 °F (316 °C), but usage is not limited to such applications (see 8.3).
Certain processing procedures and service conditions may cause these castings to become subject to stresscorrosion cracking; ARP1110 recommends practices to minimize such conditions. Where stress-corrosion is considered to be a factor, precipitation heat treatment should be performed at a temperature not lower than 1000 °F (538 °C).
This specification covers a corrosion-resistant steel in the form of investment castings.
Application
These castings have been used typically for parts which will be machined in the solution heat treated condition and, after precipitation heat treatment, will require good corrosion resistance and strength up to 600 °F (316 °C), but usage is not limited to such applications (see 8.3).
Certain processing procedures and service conditions may cause these castings to become subject to stresscorrosion cracking; ARP1110 recommends practices to minimize such conditions. Where stress-corrosion is considered to be a factor, precipitation heat treatment should be performed at a temperature not lower than 1000 °F (538 °C).
SAE AMS5357 Revision D, June 1, 2017
Steel, Corrosion-Resistant, Investment Castings 15Cr - 4.6Ni - 0.22Cb -
2.8Cu Solution Heat Treated, Precipitation Hardenable