SAE AMS5355
$78.00
$35.10
Save 55%
SAE AMS5355 Revision J, October 1, 2009
Steel, Corrosion Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb -
3.2Cu Homogenization and Solution Heat Treated or Homogenization, Solution,
and Precipitation Heat Treated
Description / Abstract:
Form
This specification covers a corrosion resistant steel in the form of investment castings.
Application
These castings have been used typically for parts requiring good corrosion resistance and strength up to 600 °F (316 °C), but usage is not limited to such applications (See 8.3).
Certain processing procedures and service conditions may cause these castings to become subject to stresscorrosion cracking; ARP1110 recommends practices to minimize such conditions. Where stress-corrosion is considered to be a factor, precipitation heat treatment should be performed at a temperature not lower than 1000 °F (538 °C).
This specification covers a corrosion resistant steel in the form of investment castings.
Application
These castings have been used typically for parts requiring good corrosion resistance and strength up to 600 °F (316 °C), but usage is not limited to such applications (See 8.3).
Certain processing procedures and service conditions may cause these castings to become subject to stresscorrosion cracking; ARP1110 recommends practices to minimize such conditions. Where stress-corrosion is considered to be a factor, precipitation heat treatment should be performed at a temperature not lower than 1000 °F (538 °C).
SAE AMS5355 Revision J, October 1, 2009
Steel, Corrosion Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb -
3.2Cu Homogenization and Solution Heat Treated or Homogenization, Solution,
and Precipitation Heat Treated